CUT3255 Cemented Carbide ISO Brazed Tips

Type

Dimensions (mm)

L

t

S

r

α°

B10

10

6

4

4

18

B12

12

8

5

5

18

B16

16

10

6

6

18

B20

20

12

7

7

18

B25

25

14

8

8

18

B32

32

18

10

10

18

B40

40

22

12

12

18

B50

50

25

14

14

18

ISO Code

Grade

Physical and Mechanical Properties

Recommended Applications

Density
g/cm3

Hardness
HRA

TRS
N/mm2

P10

YT15

11.3

91.5

1700

For the finishing of steel and cast steel. High cutting speed and medium feed rate are recommended.

P20

YT14

11.4

90.5

1600

For the semi-finishing of steel and cast steel.

P25

YZ25

13

91.5

2000

For milling processes of steel and cast steel.

P30

YT5

12.9

89.5

2000

For heavy machining of steel and cast steel, rough machining at medium and low speeds.

P40

YM40

13.1

90.5

2300

For heavy turning of steel and cast steel, also suitable for face milling.

M05

YS8
YM05

13.4
13.8

92.5
92

1600
1800

For the finishing of high-temperature alloys based on iron, cobalt, and nickel, as well as high-strength steel. Also suitable for finishing of hard cast iron, high-manganese steel, and heat-treated steel.

M10

JW1

13.1

91.5

1500

For the finishing and semi-finishing of stainless steel and general corrosion-resistant steel.

M20

JW2

13

90.5

1700

For the preliminary finishing and light rough machining of stainless steel, alloy steel, and high-manganese steel.

K05

T04F
(YG3X)
YG3

15.0
15.0

92
90.6

1800
1600

For the finishing of cast iron, non-ferrous metals, heat-resistant alloys, and titanium alloys.

K10

YG6X
YG6A

15.0
14.8

91.0
91.5

1800
1700

For finishing and semi-finishing to light rough machining of cast iron, non-ferrous metal, heat-resistant alloys, and titanium alloys.

K20

YG6

14.9

89.5

1800

For finishing and light rough machining of cast iron, heat-resistant non-ferrous metal alloys, and titanium alloys.

K30

YF8

14.7

89

2000

For preliminary finishing and rough machining of cast iron, non-ferrous metals, heat-resistant alloys, and titanium alloys under continuous and intermittent machining conditions.