1000mL Yttria Stabilised Zirconia Glass with Lid Description:
Zirconia Ceramic Properties:
Density: 6,05 g/cm³
Water Absorption: <0,05%
Firing Temperature: 1550 °C
Hardness: 1350 HV
Flexural Strength: 950 MPa
Compressive Strength: 25 000 MPa
Fracture Toughness: 6–8 MPa·m^(1/2)
Coefficient of Thermal Expansion: 9,5x10⁻⁶/°C
Alternate Names for the Yttria Stabilised Zirconia Jar: Yttria Stabilised Zirconia Grinding Jar (YSZ Grinding Jar), Zirconia Jar and Zirconium Oxide Jar.
The Advantages of the Yttria Stabilised Zirconia Grinding Jar and Grinding Media Include:
- High density
- High hardness and toughness, 60 times harder than standard steel
- High thermal expansion
- Low thermal conductivity
- Impact resistance
- High corrosion and wear resistance

1000mL Yttria Stabilised Zirconia Glass with Lid Specifications:
|
TYP-MQ
|
TYP-GT
|
Capacity
|
1000ml
|
1000ml
|
External Diameter
|
123mm
|
120mm
|
Height
|
123mm
|
132 mm
|
Wall Thickness
|
8mm
|
8mm
|
Lid Thickness
|
8mm
|
8mm
|
The dimensions provided above are for reference only. Contact us for precise specifications or customised enquiries.
*Grinding Ball Recommendation: When using the 1000mL YSZ Glass, 1 000 pieces of 5mm diameter balls, or 200 pieces of 10mm diameter balls, or 3 pieces of 20mm diameter balls are recommended.
1000mL Yttria Stabilised Zirconia Glass with Lid Applications:
- Yttria Stabilised Zirconia (YSZ) grinding jars are used for milling materials to produce finely divided powders for use in mineral processing, paints, pyrotechnics, ceramics and selective laser sintering.
- Zirconia jars and zirconia balls maintain stability and exhibit adequate abrasion resistance, thereby preventing contamination during milling in a ball mill.
1000mL Yttria Stabilised Zirconia Jar with Lid Packaging:
SAM's zirconia milling vessels and YSZ milling vessels are securely packaged to minimise damage during storage and transport, thereby preserving the integrity of the product in its original condition.
Safety Data Sheet (MSDS) for your reference!