500mL Yttria Stabilized Zirconia Jar with Lid Description:
Zirconium dioxide ceramic performance:
Density: 6.05 g/cm³
Water absorption: <0.05%
Firing temperature: 1550 °C
Hardness: 1350 HV
Flexural strength: 950 MPa
Compressive strength: 25 000 MPa
Fracture toughness: 6–8 MPa·m1/2
Thermal expansion coefficient: 9.5×10^-6 /°C
Alternate names for Yttria Stabilized Zirconia Jar: Yttria Stabilized Zirconia Grinding Jar (YSZ Grinding Jar), Zirconia Jar and Zirconium Oxide Jar.
The advantages of Yttria Stabilized Zirconia Grinding Jar and Grinding Media include:
- High density
- High hardness and toughness, being 60 times harder than standard steel
- High thermal expansion
- Low thermal conductivity
- Impact resistance
- High corrosion and wear resistance

500mL Yttria Stabilized Zirconia Jar with Lid Specifications:
|
TYP-MQ
|
TYP-GT
|
Capacity
|
500ml
|
500ml
|
Outer Diameter
|
106mm
|
106mm
|
Height
|
106mm
|
96 mm
|
Wall Thickness
|
8mm
|
8mm
|
Lid Thickness
|
7mm
|
7 mm
|
The aforementioned dimensions are provided as a reference. Please contact us for precise specifications or customised inquiries.
*Milling Ball Recommendation: For a 500mL YSZ Jar, it is recommended to use 500 pieces of 5 mm diameter balls, or 100 pieces of 10 mm diameter balls, or 2 pieces of 20 mm diameter balls.
500mL Yttria Stabilized Zirconia Jar with Lid Applications:
- YSZ milling jars are employed to grind materials into extremely fine powders for use in mineral processing, paints, pyrotechnics, ceramics and selective laser sintering.
- Zirconium dioxide jars and zirconium dioxide balls exhibit stability and possess good abrasion resistance, thereby preventing contamination with other impurities during ball milling.
500mL Yttria Stabilized Zirconia Jar with Lid Packaging:
SAM's zirconia milling jars and YSZ milling jars are carefully processed to minimise damage during storage and transport, thereby preserving the original quality of our products.
Safety Data Sheet (MSDS) for your reference!